| Cellulose ether for construction use |
|
 Cellulose ether for construction use-Hydroxy Propyl Methyl Cellulose(HPMC) |
| Composition and chemi1cal structure |
|
| Technical index |
Quality Standard: Q/79339844-1.01-2008
Index name |
Model |
KH60 |
KH65 |
KH75 |
Methoxy（WT%） |
28.0－30.0 |
27.0－30.0 |
19.0－24.0 |
Hydroxypropoxy（WT%） |
7.0－12.0 |
4.0－7.5 |
4.0－12.0 |
Gelling temperature（℃） |
58.0－64.0 |
62.0－68.0 |
70.0－90.0 |
Moisture（WT%） |
≤5.0 |
Residue on ignition（WT%） |
≤1.0 |
PH Value（1% solution , 25℃） |
5.0－7.5 |
Viscosity Standard（2% solution , 20℃）,NDJ-8S
NDJ-1 2% solution 20℃ |
B type Viscosimeter 2% solution 20℃ |
Nominal Viscosity(mPa.s) |
Range |
Nominal Viscosity(mPa.s) |
Range |
5 |
3-9 |
15000 |
13000-17000 |
| 15 |
10-20 |
20000 |
18000-22000 |
| 25 |
20-30 |
30000 |
23000-34000 |
| 50 |
40-60 |
40000 |
35000-45000 |
| 100 |
80-120 |
50000 |
46000-55000 |
| 400 |
300-500 |
60000 |
56000-64000 |
| 800 |
700-900 |
75000 |
65000-85000 |
| 1500 |
1200-2000 |
80000 |
75000-85000 |
| 4000 |
3500-4500 |
10万 |
85000-130000 |
| 8000 |
7000-9000 |
150000 |
130000-180000 |
| 10000 |
9000-11000 |
200000 |
180000 or more |
|
| Properties: |
1.Appearance: HPMC is white or similar to white fiber or granular powder; odorless .
2.Properties: almost insoluble in ethanol, ether and acetone; quickly dispersed in 80-90℃ water; aqueous solution is very stable in room temperature; has good wetting/dispersing/adheisve/thickening/emlusifying/water preserving/film-forming properties; can prevent the infilration of grease; film formed has excellent flexibility and trransparency; has good compatibility with other emulsifier; easy salting-out. its solution is stable with PH 2－12.
3.Apparent density: 0.30－0.70g/cm3, density is 1.3g/cm3. |
| Dissolving process |
HPMC will agglomerate when directly added to water and then dissolve. In this way it dissolves very slow and hard. Suggested methods as followers:
1. In hot water.
HPMC does not dissolve in hot water. The primary HPMC can be uniformly disperse in hot water. Then cool down in two ways:
a) Add hot water in container and heated to over 70℃. Add HPMC gradually while slowly, stir. At the beginning, HPMC float on the top of water, then turns into slurry state stir and cool down.
b) Add water in container to 1/3 or 2/3 of its content. Heated to over 70℃ add HPMC by sequence of a). Make it disperse to form slurry state. Add cool water or ice to the resideual content, stir and cool down the mixture.
2. Powder combination.
Mix HPMC with identical volume of other powder, disperses them sufficiently then add water to the |
| Application |
It is widel used as thickener, adhesive, water preserving agent, film-forming agent in construction, building materials, dispersion coating, wallpaper paste, polymerization aids, leathers, printing ink and paper making etc.l also used in petroleum drilling and daily-use chemicals |
| Packing |
Packed in 25kgs complex paper bag inner with PE bag, bags are wrapped tightly in pallets. Stored indoors in dry and draughty place, avoid rain and sunlight during transporting. |
|
|